NKC164-1/4H NKC164E-1/4H銅合金高強度耐腐蝕耐磨

NS 16544? Norwegian standard / NS? Cu Pb20 Sn 5, (Cu Sn5 Pb20-V), CC497K

NS 16550? Norwegian standard / NS? SS 5144 (Cu Zn33 Pb2), CC750S

NS 16554? Norwegian standard / NS? SS 5253 (Cu Zn39 Pb2 Al), CB754S, CC754S

NS 16565? Norwegian standard / NS? SS 5256 (Cu Zn35 Al1), ~CW710R? (CuZn35Ni2)?

NS 16570-15? Norwegian standard / NS? SS 5716-15 (Cu Al10 Ni5 Fe4 F70), AB-200

NS 16570-20? Norwegian standard / NS? SS 5716-20 (Cu Al10 Ni5 Fe4 F74), AB-220 Ni

LM’s comparison list between different

norms from Copper alloys

Please read below on the wished for trade-name in the left hand column, and get it translated into LM-language on the right-hand

column. The right hand column with our name is either identical in composition or a fully replaceable alloy with only minor

differences. The column in the middle states the norm and its country of origin.

With no marks in front of LM’s alloy = alloy is identical, with this sign “~” = alloy is very similar, fully replaceable.

QAL7：具有高的強度和 性，在大氣、淡水、海水和某些酸中耐蝕性高，可熱、冷態(tài)壓力加工，可電焊和氣焊，不易釬焊。

用途： 簧盒要求耐蝕的其它 性元件。

QAL9-4：具有高的強度，良好的減摩性和很好的耐蝕性，可熱加工，可焊接，但不易釬焊。

用途：高強、耐磨零件，如軸承、軸套、齒輪、渦輪等；還可制造接管嘴、法蘭盤、扁形搖臂、支架等。

QAL10-4-4：在400℃以下具有穩(wěn)定的力學性能，有良好的減摩性，在大氣、淡水、海水中耐蝕性很好，可熱加工，可焊接，但不易釬焊。

用途：高強度的耐磨零件盒在400℃以下工作的零件，如軸承、軸套、齒輪、球形座、螺帽、法蘭盤等。

主要分析方法：化學成分的影響

化學成分對鋁青銅組織與性能的影響一直是關(guān)注的熱點之一。首先，化學成分對合金作用的好與壞并沒有一個明確的界定。如鐵加入鋁青銅中一般起到細化晶粒、減小“自發(fā)回火脆性”、提高力學性能的作用，但當鐵含量較高時，鐵會以Fe3Al2化合物析出，使合金的機械性能變壞，因此鐵含量不應超過5%。還有鋅元素，很多研究認為它與基體金屬固溶后，可提高金屬的塑性，而也有研究認為其為雜質(zhì)元素。由此看出，合金元素的作用不能一概而論。普遍認為加入適量的合金元素可改善合金的機械性能，如加入適量的鐵形成鋁鐵青銅，加入錳形成鋁錳青銅，加入鎳形成鋁鎳青銅。其次，對于雜質(zhì)元素含量的要求還沒有一個明確的界定。正是由于化學成分的變化才使得鋁青銅的種類和應用場合各不相同，研究者應該不斷研究化學成分的影響、作用機理，進一步擴大鋁青銅的應用范圍。

強化